Tough high melt flow polyamides

ABSTRACT

Tough, high melt flow, low molecular weight polyamide compositions containing toughening polymers are obtained by blending conventional polyamides with the toughening polymer and then mixing the blend with very low molecular weight polyamides which are capable of reacting with the conventional polyamide by transamidation.

This is a division of application Ser. No. 07/489,774, filed Mar. 5, 1990, now U.S. Pat. No. 5,112,908, which is a continuation of application Ser. No. 07/945,518, filed Dec. 23, 1986, now abandoned.

FIELD OF THE INVENTION

This invention relates to thermoplastic polyamide compositions having high melt flow to facilitate flow into complex, thin molds, and which unexpectedly have good impact toughness; and to processes for preparing such compositions.

DESCRIPTION OF THE PRIOR ART

Thermoplastic polyamides have good elongation; high energy to break, as demonstrated in tensile tests; high tensile impact strength and high energy absorption as demonstrated in falling dart tests, e.g., the Gardner impact test However, in one aspect of toughness, polyamides are quite deficient; namely, in resistance to crack propagation This deficiency is reflected in notch sensitivity, brittle breaks and occasional catastrophic failure of molded or extruded parts. This tendency of polyamides to break in a brittle manner with crack propagation, rather than in a ductile fashion is a significant limitation on utility. Polyamides may be characterized in their brittleness by performance in the notched Izod test, ASTM D-256-56. With the normal notch radius of 10 mils, polyhexamethylene adipamide (66 nylon), dry as molded, will have a notched Izod value of about 1 ft. lb/inch of notch (53 joules/meter).

Recently, it was discovered that certain tougheners could be blended with polyamides of normal molecular weight, i.e., usually over 10,000, and normal melt flow, i.e., less than 200 gm/per 10 minutes and generally less than 100 gm per 10 minutes, to greatly improve resistance to crack propagation. This discovery is described in Epstein, U.S. Pat. No. 4,174,358. In this patent, polyamides having melt flows in the usual range of 0.01 to 200 grams per 10 minutes (at 280° C. and 2160 g load using ASTM D-1238) and having molecular weights of over 5,000 and usually over 10,000 (the lowest exemplified is 10,300) are melt blended with small particles of low tensile modulus copolymers that have adherent sites to obtain a highly toughened polyamide material.

There are applications where it is desirable to use polyamides of unusually high melt flow, i.e., flows of over 200 grams per 10 minutes, and having low molecular weights (which facilitate melt flow) i.e., below 8,000. Such applications include ones where molten polyamide must flow into very thin molds, such as, instrument consoles, pen barrels, etc. However, it is generally understood by those skilled in the art that linear aliphatic thermoplastic polyamides with molecular weights below 10,000 and melt viscosities below 1,000 poise (or melt flow above about 70 gm per 10 minutes or inherent viscosity below 1 dl/gm) are too brittle for ordinary use even though they have the advantage of better processability, and little attention has been directed to them in the industrial area and even in academic circles.

There have bee a large number of patents published addressed to toughening conventional polyamides, i.e., ones of high molecular weight and low flow, for injection molding, and substantial advances have been made in toughness of these materials; however, very little attention has been paid to the equally important problem of providing polyamides that are not only tough, but which are also high flow materials that can be easily molded into large parts with complex shapes in thin sections and with long flow paths.

It is the object of this invention to provide toughened polyamides where the polyamide is a high melt flow, low molecular weight polyamide. It is another object of the invention to provide processes for obtaining such toughened polyamides.

SUMMARY OF THE INVENTION

The toughened polyamides of this invention are multiphase thermoplastic blends comprising:

a) 60-90 wt. %, preferably 70-90 wt. %, of a polyamide matrix wherein at least 50% (preferably 75%) of the polyamide matrix by weight is composed of aliphatic moieties, wherein the number average molecular weight of the polyamide(s) in the matrix is between 3,000 and 8,000, preferably 5,000, and

b) complementally, 10-40 wt. %, preferably 10-30 wt. %, of at least one organic polymeric toughener having a tensile modulus below 10,000 psi or for a mixture of tougheners an average modulus below 10,000 psi, preferably below 5,000 psi and most preferably below 3,000 psi, for either the single toughener or the mixture, and having a number average particle size less than 1,000 nanometers, and preferably less than 500 nanometers,

and wherein the blend has a notched Izod of over 2 ft. lbs/inch, and also has a tensile strength and melt flow such that the product of notched Izod in ft. lb/inch, tensile strength in thousands of pounds/in² and flow in grams/10 minutes is greater than 5,000, preferably greater than 10,000, and has 0.5-15 weight percent, preferably 1-7 weight percent, of the polyamide matrix grafted to or entrapped in the rubber.

The process o this invention comprises:

1. mixing a high molecular weight polyamide, or mixtures of such polyamides, having a number average molecular weight over 10,000, and having an inherent viscosity greater than 0.7 deciliters/gm, with an organic polymeric toughener having a tensile modulus below 10,000 psi or a mixture of tougheners having an average tensile modulus below 10,000 psi, preferably below 5,000 psi, and most preferably below 3,000 psi, and having graft sites, in a dispersing device at shear forces sufficient to disperse the toughener in the polyamide

2. blending into the blend obtained in step 1 a low molecular weight polyamide which will react by transamidation, i.e., having a number average molecular weight below 5,000 and having an inherent viscosity less than 0.5, i.e., so that the number average molecular weight of the entire matrix is below 8,000.

The high and the low molecular weight polyamides are chosen such that in the matrix resulting from transamidation, at least 50% and preferably at least 75% of the polyamide matrix is composed of aliphatic moieties.

The low molecular weight polyamide is preferably chosen to have a sufficiently low molecular weight and sufficiently high combination of unbalanced ends and capped ends or sufficiently high end group imbalance to result, after reaction with the high molecular weight polyamide, in a polyamide matrix wherein the sum of the unbalanced ends and any capped ends is at least 200 equivalents per 10⁶ grams of polyamide, or wherein the end group imbalance is at least about 1.9/1 or more and the sum of said ends is greater than 100. Such end group imbalance or a high concentration of unbalanced and capped ends is convenient in order for the polyamide matrix to be maintained a low molecular weight during the molding operation at the low moisture levels required to avoid surface imperfections (splay) at low molding pressures employed with the unreinforced compositions.

An advantage of the blends of this invention is that they can be molded at a fraction of the pressures needed to mold conventional higher molecular weight polyamides. Conventional polyamides generally have melt viscosities in the range of 100 to 1,000 Pascal seconds (i.e., melt flows of 5 to 70 grams/10 minutes) and injection pressures of over 1,000 psi are needed to force the polyamides into molds. This necessitates use of expensive specialized high pressure molding equipment. In contrast, the polyamide blends of this invention have melt viscosities between about 5 and 50 Pascal seconds (50-500 poise) or melt flow greater than 100 g/10 min. and generally greater than 200 g/10 min. and can be molded at injection pressures of less than 1,000 psi.

DESCRIPTION OF THE INVENTION

Because of their low viscosity, the compositions of this invention can be processed at molding pressures up to an order of magnitude lower than those conventionally employed, providing great economies in molds and molding machines as well as expanding the range of polyamide resins which may be molded practically. They can also be injection molded at conventional pressures when they contain unusually high concentrations of fibrous reinforcement, e.g., on the order of 50 volume %.

In the toughened, multiphase thermoplastic compositions of this invention the polyamide matrix will comprise 60 to 90 percent by weight of the composition, more than half and preferably more than 75% of the polyamide by weight will be aliphatic. The polyamide will have a number average molecular weight of 3,000 to 8,000 and preferably will either have an end group imbalance of at least about 1.9/1 or more and the sum of unbalanced and capped ends is greater than 100 g/10⁶ gm of polymer, or have more than 200 equivalents of the sum of unbalanced ends and capped ends per 10⁶ gm of polyamide. The toughener will complementally be 10 to 40% by weight and grafted to 0.5 to 15% of the polyamide matrix including enhanced polyamide. The toughener polymer phase will have a tensile modulus of 10 to 10,000 psi and may be either a branched or straight chain polymer. The toughener is dispersed to a number average preferably less than 1 micron and most preferably less than 0.5 micron, recognizing that a second component of toughener with larger particle size comprising up to the order of 5% of the composition would not make a major difference in the performance of the composite. The toughened compositions of this invention have a uniquely favorable balance of toughness (preferably a notched Izod at least 5 ft lbs/inch) and processability (melt flow at least 100 gms and generally at least 200 gms/10 minutes at 280.C and 2160 grams weight in ASTM D-1238-73) and can be molded under low pressure, generally under 1,000 psi and preferably under 500 psi, and into large thin parts with long flow length.

The utility of these compositions derives from the unusually good combination of very high melt flow combined with unexpectedly good toughness for materials with such low molecular weight. The toughened high flow thermoplastic compositions can be molded under low pressure into a wide range of useful articles such as cabinets, instrument consoles, automotive exterior parts, tractor and truck consoles, sleds, stretchers, boats, pen barrels, louvres and the like, and a variety of parts with large surface area and thin sections.

The high molecular weight polyamides and the low molecular weight polyamides used to make the compositions of this invention are well known in the art and embrace those semicrystalline resins commonly referred to as nylons. Suitable polyamides include those described in U.S. Pat. Nos. 2,071,250; 2,071,251; 2,130,523; 2,130,948; 2,241,322; 2,312,966; 2,512,606; and 3,393,210.

The high molecular weight polyamides can be produced by condensation of equimolar amounts of a saturated dicarboxylic acid containing from 4 to 12 carbon atoms with a diamine, in which the diamine contains from 4 to 14 carbon atoms, or by condensation of lactams containing from 4 to 12 carbon atoms.

The low molecular weight polyamides are prepared by polymerization in conventional equipment and employing recipes containing a large excess of either diacid or diamine and/or substantial amount of monofunctional acid or amine to give the end groups specified above. Alternatively, the low molecular weight polyamide may be prepared by depolymerizing high molecular weight nylon generally above the melting point in the presence of oligomeric or monomeric mono and difunctional acids or amines as described above. Optionally, water and catalysts may be added.

Examples of polyamides, whether high or low molecular weight, include polyhexamethylene adipamide (66 nylon), polyhexamethylene azelaamide (69 nylon), polyhexamethylene sebacamide (610 nylon), and polyhexamethylene dodecanoamide (612 nylon), the polyamide produced by ring openings of lactams, i.e., polycaprolactam, polylauric lactam, poly-11-aminoundecanoic acid, bis(paraaminocyclohexyl) methane dodecanoamide. It is also possible to use in this invention mixtures of polyamides and polyamides prepared by the copolymerization of two of the above polymers or terpolymerization of the above polymers or their components, e.g., for example, a polyhexamethylene adipamide/polycaprolactam copolymer or an adipic/isophthalic acid/hexamethylene diamine copolymer with the limitation that aliphatic polyamide will comprise more than half and preferably more than 75% the matrix of the composition as initially prepared. Preferably, the polyamides are linear with a melting point in excess of 200° C.

To maintain stable, low number average molecular weight it is convenient for the polyamide matrix to have an imbalance of ends of at least about 1.9/1 or more and at least 100 equivalents of unbalanced ends per 10⁶ grams of polyamide, or that it contain a minimum of 200 equivalents of unbalanced ends and capped ends per 10⁶ grams of polyamide.

At the low molding pressures used with the polyamide blends of this invention, water levels conventionally acceptable (about 0.18%) in the molding blends will cause surface imperfections. Therefore, water levels below 0.1% are preferred. At these low water levels polyamide with balanced, uncapped ends will polymerize in the melt to approach the corresponding equilibrium molecular weight. In order to insure stabilization of the resins at low molecular weights, they must have an excess of either amine or carboxyl ends (unbalanced ends) or capped ends. It is preferred that the low molecular weight polyamide will have a combination of unbalanced ends and capped ends, if any, sufficient to result in the sum of the unbalanced ends and capped ends being at least 200 equivalents/10⁶ grams of polyamide. For example, if ##EQU1## and if the number of Capped Ends=110, then the sum is 210 ends.

The composition is toughened by the combination of at least one toughening polymer with the polyamide. The term "at least one toughener" means one or more polymers which coexist in single discrete particles having a requisite particle size. The toughening polymer or the mixture of polymers should have :

(a) sites which are grafted to the polyamide matrix so that 0.5-15 weight % and preferably 1-7 weight % of the polyamide matrix is either grafted or entrapped in the toughening polymer;

(b) tensile modulus, as added, in the range of about 10 to 10,000 psi, preferably about 10 to 5,000 psi, most preferably about 10 to 3,000 psi.

The polyamide is a continuous phase in the composition and the toughening polymer performs the function of a soft dispersed phase which is grafted to the polyamide matrix. The toughening polymer may be elastomeric, but it has been found that some thermoplastic polymers which are not elastomeric are also effective in the compositions.

The toughening polymers are branched or straight chain and are of such composition that crosslinking other than by grafting to the polyamide matrix is not necessary to their function and excessive crosslinking may, in fact, be harmful. Preferably the toughener particles will have a median size below 1000 nanometers, and most preferably a median size below 500 nanometers as measured by small angle x-ray scattering (SAXS).

Any toughening polymer phase which has the required tensile modulus, dispersed particle size and has graft sites to adhere to 0.5 to 15 wt. % and generally less than 7% of the polyamide matrix will confer the desired characteristic of toughness without excessively impairing high flow of the thermoplastic composition. Preferably, the graft sites will be present in the toughener as metal neutralized carboxyl, adjacent carboxyl, anhydride or epoxy functional groups, but other functional sites such as sulfonic acid or amine may be effective. These sites will be present in amounts that provide the requisite grafting. The concentration of graft sites will be

(i) 1.6-2.4 weight % of blend when the sites are metal neutralized carboxyl sites and the sites are 25-65% neutralized;

(ii) 0.02-0.1 weight % of blend when the sites are adjacent carboxyl or anhydride sites; and

(iii) 0.4-1.6 weight % of blend when the graft sites are epoxy sites.

Examples of some toughening agents include

(1) polymers of ethylene, at least one alpha-olefin of 3 to 6 carbon atoms, and at least one unsaturated monomer taken from the class consisting of branched, straight chain and cyclic hydrocarbon compounds having from 4 to 14 carbon atoms and having at least one additional nonconjugated unsaturated carbon-carbon bond, in which said polymer has grafted thereto an unsaturated monomer taken from the class consisting of

(a) alpha,beta-ethylenically unsaturated dicarboxylic acids having from 3 to 10 carbon atoms,

(b) monoesterified esters of such acids where the alcohol moiety contains 1 to 29 carbon atoms,

(c) anhydrides of dicarboxylic acids covered in (a), and

(d) metal salts of dicarboxylic acids and the monoesters of said dicarboxylic acid covered in (a) and (b) having from 0 to 100 percent of the carboxylic groups ionized by neutralization with metal ions.

Preferably, the polymer can be a copolymer of ethylene, propylene and 1,4-hexadiene and, optionally, norbornadiene, said copolymer having grafted thereto an unsaturated monomer taken from the class consisting of fumaric acid, maleic acid, maleic anhydride, the monoalkyl ester of said acids in which the alkyl group of the ester has 1 to 3 carbon atoms (one said polymer is grafted "Nordel" (Du Pont Co.));

(2) copolymers of ethylene, methyl or ethyl acrylate, and from about 0.0025-0.077 mole/100 g polymer of a mono alkyl ester of 1,4-butenedioic acid in which the alkyl group of the ester has 1 to 6 carbon atoms and having 0 to 100 percent of the esters of 1,4-butenedioic acid ionized by neutralization with metal ions selected from lithium, sodium, potassium, calcium and zinc ions (for example, one such polymer is "Vamac" (Du Pont Co.));

(3) ionic copolymers of units derived from alpha-olefin having the formula RCH═CH₂ wherein R is H or alkyl having from 1 to 8 carbon atoms and from 0.2 to 25 mole percent of units derived from an alpha,beta-ethylenically unsaturated mono- or dicarboxylic acid, at least 10% of the acid groups of said units being neutralized by metal ions having a valence of from 1 to 3, inclusive. Preferably, the copolymer will be made of ethylene and acrylic or methacrylic acid. For example, one such polymer is "Surlyn" (Du Pont Co.).

(4) Organic polymers which contain graft sites and sufficient alkyl acrylate, butadiene or substituted butadiene, isoprene, isobutylene, or similar rubber producing monomers to achieve the desired modulus.

Useful specific polymers for toughening polyamide compositions include: zinc salt of ethylene/isobutyl acrylate/methacrylic acid; ethylene/methyl acrylate/monoethyl ester of maleic anhydride that is 0 to 100 percent neutralized with zinc, sodium, calcium, magnesium, lithium, antimony, or potassium salts; mixture of ethylene/isobutyl acrylate/methacrylic acid and ethylene/methyl acrylate/monoethyl ester of maleic anhydride and zinc salts thereof; ethylene/methyl acrylate/methacrylic acid and zinc salts thereof; zinc salts of ethylene/vinyl acetate/methacrylic acid; zinc salts of ethylene/methyl methacrylate/methacrylic acid; mixtures of ethylene/vinyl acetate and a zinc salt of ethylene/isobutyl acrylate/methacrylic acid; mixtures of ethylene/isobutyl acrylate and a zinc salt of ethylene/isobutyl acrylate/methacrylic acid; mixtures of ethylene/acrylic acid and ethylene/vinyl acetate; ethylene/vinyl acetate/maleic anhydride; ethylene/vinyl acetate monoethyl ester of maleic anhydride; ethylene/vinyl acetate/glycidyl methacrylate; ethylene/propylene/1,4 hexadiene-g-maleic anhydride; ethylene/propylene/1,4-hexadiene-g-nadic anhydride; mixtures of ethylene/propylene/1,4 hexadiene and ethylene/maleic anhydride; mixtures of ethylene/propylene/1,4 hexadiene and ethylene/propylene/1,4 hexadiene-g-maleic anhydride; ethylene/propylene/1,4 hexadiene/maleic anhydride neutralized with zinc rosinate; ethylene/propylene/1,4 hexadiene-g-fumaric acid; ethylene/propylene/1,4 hexadiene norbornadiene-g-maleic anhydride; ethylene/propylene/1,4 hexadiene/norbornadiene-g-monoethyl ester of maleic anhydride; ethylene/propylene/1,4 hexadiene/norbornadiene-g-fumaric acid; mixtures of ethylene/propylene/1,4 hexadiene and ethylene/monoethyl ester of maleic anhydride; mixtures of ethylene/propylene/1,4 hexadiene and ethylene/butyl hydrogen maleate; mixtures of ethylene/propylene/1,4 hexadiene and ethylene/maleic anhydride, mixtures of butadiene/acrylonitrile and styrene/maleic anhydride; mixtures of styrene/butadiene and ethylene/maleic anhydride; mixtures of ethylene/propylene/1,4 hexadiene/norbornadiene and styrene/maleic anhydride; isoprene/phthalic anhydride; mixtures of natural rubber and ethylene/monoethyl ester of maleic anhydride; butyl acrylate/monoethyl ester of fumaric acid; ethyl acrylate/fumaric acid; mixtures of ethylene/propylene and ethylene/monoethyl ester of maleic anhydride; ethylene/propylene/5-ethylidene-2-norbornene-g-fumaric acid, ethylene/propylene/dicyclopentadiene-g-monoethyl ester of maleic acid, ethylene/propylene/5-propylene-2-norbornene-g-maleic anhydride, ethylene/propylene/tetrahydroindene-g-fumaric acid, ethylene/propylene/1,4 hexadiene/5-ethylidene-2-norbornene-g-fumaric acid with concentrations and distribution of the monomers adjusted to achieve the desired modulus and grafting to the polyamide.

It is possible to mix two or more toughener polymers together, e.g., where at least one is the source of graft sites, and the other possibly being a diluent. Mixing may be accomplished by combining the polymers with the high molecular weight polyamide separately or in combination with the proviso that the polymer containing the graft sites must not be combined with the polyamide matrix resin prior to combination of any other polymers. In ethylene/propylene/diene polymers molecular weights equivalent to melt flow of 0.5 to 400 g/10 mins and more by ASTM D-1238 but at 280° C. and a total load of 2160 g are effective.

The melt flow of the compositions of this invention are greater than 100 grams per 10 minutes and preferably greater than 200 grams per 10 minutes measured by ASTM D-1238 at 280° C. and 2160 gram load, and the toughness as characterized by notched Izod is greater than 2 ft lbs/inch, preferably greater than 5, and most preferably, greater than 8. It is noted that flows greater than 1,000 grams/10 minutes are difficult to determine precisely with efflux times less than 5 seconds. Individual determinations do not vary more than 50% around an average when care is taken to maintain moisture level in the sample well below 0.05 weight %.

The balance of mechanical properties and processability of the compositions of the invention may be represented by the product of tensile strength (T.S.) in thousands of pounds/in², notched Izod in ft. lbs/in. and flow in gm/10 minutes. In the same units this product for "Zytel" 101, a commercial, unmodified nylon and for "Zytel" 801, a commercial toughened nylon, is in the range of 500 to 1,000. For the compositions of the present invention, the product of the three is at least 5,000, preferably 10,000 with a minimum notched Izod of 2 foot pounds per inch. This is several times as good as commercial compositions.

The compositions of the invention may be modified by one or more conventional additives such as stabilizers and inhibitors of oxidative, thermal, and ultraviolet light degradation; lubricants and mold release agents, colorants including dyes and pigments, fibrous and particulate fillers and reinforcements, nucleating agents, foaming agents, plasticizers, etc.

A preferred reinforcing filler is glass fiber. A particular virtue of the compositions of this invention is their ability to maintain adequate flow while containing unusually high levels of such reinforcing filler.

The toughened compositions of this invention can be prepared by melt blending, in a closed system, a polyamide and at least one toughener polymer in a uniform mixture in a multi-screw extruder such as a Werner Pfleiderer extruder having generally 2-5 kneading blocks and at least one reverse pitch to generate high shear, or other conventional dispersing devices such as a Brabender, Banbury mill, or the like.

EXAMPLES - GENERAL PROCEDURE

The high molecular weight polyamides are prepared by conventional methods. The low molecular weight polyamides are prepared by conventional methods using the ingredients given in Table 2.

High molecular weight polyamide and toughener are dry blended and extruded to disperse the toughener. Then low molecular weight polyamide is added to reduce the molecular weight of the polyamide matrix. The high molecular weight polyamide/toughener mixture and low molecular weight polyamide in dry form are mixed after weighing in the proper proportions. The mixture is then blended in a 28 or 83 mm tri-lobal or 30 mm bi-lobal Werner Pfleiderer extruder in which the hopper is blanketed with nitrogen and the vacuum port maintained at about 25 to 30 inches vacuum. In some experiments with unextracted 6 nylon, residual monomer plugged the vacuum port causing reduced vacuum. In these cases, the residual caprolactam reduced the modulus of the final product. Extruder barrel temperatures on the smaller machines are set to rise from about 100° C. at the feed end to about 260° to 270° C. at the front end of the extruder and to 280° C. at the die, yielding melt temperatures of the blends in the range of 280° C. to about 360° C.

In some cases, the composition is formed in a single extrusion by preparing the first blend in the rear of the extruder and feeding the low molecular weight material as a sidestream.

The beading exiting the extruder is water quenched, cut and vacuum dried overnight (about 20-25 inches Hg with an N₂ bleed) at 80° C. prior to molding. Test bars, 1/2×5×1/8 inch and tensile bars are molded in a 6 oz. injection molding machine. Hold-up times are usually about 5-6 minutes. Because of the radically better flow, the force of the spring on the bypass of the hydraulic system is reduced to permit operation at reduced pressures and a gage installed to read the low pressures. Rear barrel tempratures are set to 270°-280° C. rising to 280° C. at the front. Nozzle temperatures are set at 280°-290° C. The molds are heated by water having an inlet temperature of about 90° C. Molding is carried out with fast injection and a 20/20 or 20/30 molding cycle (seconds ram forward/second hold). The molded bars are tested using the following test procedures at room temperature in the dry-as-molded state.

EXAMPLES - TEST PROCEDURES

Notched Izod toughness: ASTM D-256-56 was followed, but with the average values of 3 bars taken at each end.

Tensile Strength: ASTM D-638-58T

Elongation: ASTM D-638-58T

Flexural Modulus: ASTM D-790-58T

Tensile Modulus of the polymers: ASTM D-882 (50% RH)

Melt Flow: ASTM D-1238-73 at 280° C. and 2160 gram load. Holdup in the melt indexer or is 3 minutes for molded bars and 8 minutes for molding resin.

Particle Size: Transmission electron microscope (TEM) on slices approximately 100 nanometers thick stained with phosphotungstic acid, and small angle x-ray scattering (SAXS).

Particle size is determined by small-angle x-ray scattering, according to the following technique: The small-angle x-ray scattering (SAXS) data should be acquired on a high-resolution instrument such as the one originally designed by Bonse and Hart Zeit. fur Physik, 189, 151 (1966), and subsequently manufactured commercially by Advanced Metals Research Corporation, Burlington, Mass., as the AMR Model 6-220 x-ray Low Angle Scattering Goniometer. A suitable sample of polyamide containing dispersed toughener particles consists of a molding (generally an injection-molded tensile or flex bar) of such thickness as to transmit about 1/e (1/2.71828 or 0.368) of a CuKα (wavelength=0.1542 nm) x-ray beam. This is the optimum thickness for transmission data (data acquired when the x-ray beam passes through the thickness of the sample along the surface normal), and is generally of the order of 80 mils (0.08 inches or about 2 mm) for a typical sample. A typical molding is usually too thick (1/8 inch or greater) but can be thinned by sawing or milling.

Scattered x-ray intensity data are acquired in the range from 8 to 600 seconds of arc (2-theta). The AMR instrument is calibrated in seconds; this corresponds to a range of 0.002. to 0.16 or 4×10⁻⁵ to 3×10⁻³ radians. Appropriate step sizes range upwards from 2 seconds of arc as the scattering angle increases; 20 points each at step-sizes of 2, 4, 8, and 16 seconds will cover the angular range in 81 points. These are "slit-smeared" results, and, after smoothing and subtraction of instrumental background, should be "desmeared" before interpretation. For this work, the data are desmeared by the method of Schmidt and Hight, Acta Cryst. 13,480 (1960); P. W. Schmidt, Acta Cryst., 19,938 (1965) to cover the range from 0.005° to 0.07° 2-theta. (The experimental angular range from 0.07° to 0.16° of the observed data is required only to desmear the retained results below 0.07°.) The desmeared intensity results can be represented as I(h), where ##EQU2## Here, θ=(2θ)/2 and sin θ=θ in radians at these small angles, and λ=the wavelength of CuKα radiation. These intensity results are converted to the "Invariant" argument, h² I(h), by multiplying each desmeared intensity by the square of the angle of observation for that point.

A plot of the invariant argument will be characterized by having a maximum at an angle below 0.04° 2-theta if the dispersed particles causing the scattering have diameters of the order of hundreds of nanometers. If the particle-size distribution is narrow (nearly monodisperse), the particle diameter is inversely proportional to the position of this maximum: diameter=4.87/2θ°_(max) nm. If there is finite breadth to the distribution, the peak position will be shifted to lower angles and the breadth of the distribution must be taken into account. For the results cited here, the observed invariant-argument curves were matched in calculated curves derived assuming a model of a log-normal particle-size distribution. For typical distributions, the most probable particle size is of the order of 2/3 to 3/4 that calculated on the basis of the peak position of the invariant argument alone.

In order to characterize a particle-size distribution in the manner employed here, two measurements are made on the invariant-argument curve. The angular position (2-theta), h_(m), of the maximum is determined and the angular position of the "half-height" h_(h), is determined. The half-height is that point on the invariant-argument curve which has an ordinate one-half that of the maximum and is on the high-angle side of the maximum. Given a log-normal model, the breadth of the distribution, expressed in relative terms, is a function only of the ratio, R_(h), of these two angles: R_(h) =h_(h) /h_(m). (R_(h) should have a value greater than about 1.57. If it is significantly less than this, the position of the maximum of the curve has probably been displaced to higher angles by interparticle interference arising from close, regular packing of the particles.)

A log-normal distribution can be characterized by R_(s), the ratio of the size at one-sigma of the distribution to the size at the center. For this work, an expression for R_(s) was determined from R_(h) by a third order polynomial regression fit to computer-generated data. This equation is: R_(s) =1.19056+1.84535R_(h) -0.33524R_(h) ² +0.030186R_(h) ³ (Note that when R_(h) =1.5728+,R_(s) =1.00 and the distribution is monodisperse. An R_(s) of less than 1 0 has no physical meaning.)

For each distribution ratio, R_(s), there is a factor, F, which can be used to correct the apparent size derived from the position of the invariant maximum corresponding to a monodisperse "distribution". Again, a third order polynomial fit was determined from a computer-generated model: F=1.48725-0.4283R_(s) -0.062415R_(s) ² +0.022482R_(s) ³.

The scattering curve from monodisperse spherical particles can be approximated at very low angles by I(h)=k [exp (-h² R_(o) ² /3)]. (See A. Guinier & G. Fournet, Small-Angle Scattering of X-Rays, John Wiley & Sons, Inc., New York (1955) page 25), where R_(o) is the radius of gyration. The invariant argument is then kh² ·[exp (-h² R_(o) ² /3)]. From the differentiation of this expression, the condition for the maximum, h_(m) ² R_(o) ² /3=1 or ##EQU3## Substituting for ##EQU4## where λCuKα 0.15418 nm, R_(o) =0.042502/2θ_(max) if 2θ is in radians, R_(o) =2.4352/2θ_(max) if 2θ is in degrees. For the approximation used in this work, the exponential (Gaussian) fit does not extend to angles as high as represented by the maximum of the invariant argument, and a better approximation is given by: R_(o) =2.182/2θ_(max) where 2θ is in degrees. Since the diameter of a sphere, D, as a function of the radius of gyration, R_(o), is: ##EQU5## then D_(m) (nm)=5.6339/2θ·_(max). D_(m) is the diameter of a particle in a monodisperse "distribution", where all the particles are the same size. When there is a finite distribution of sizes modeled as described above, then the characteristic diameter, D_(c), is derived from D_(m) as: D_(c) =F.D_(m).

The SAXS method provides a convenient method for determining median values but is applicable only for median particle sizes below 1,000 nanometers. TEM is used for particle sizes above and below 1,000 nanometers. For several examples where the SAXS method is not applicable, particles are counted using a "quantimet" image analyses. Results are given below in Table A:

                  TABLE A                                                          ______________________________________                                                  Number       Volume                                                            Average      Average                                                           Longest      Longest    Number                                                 Dimension    Dimension  of Particles                                  Example  Nanometers   Nanometers Counted                                       ______________________________________                                         15       .22          1.12       754                                           16       .24          .95        879                                           35       .32          2.38       683                                           38       .49          2.63       372                                           54       .26          1.10       746                                           ______________________________________                                    

Although theories are still somewhat speculative, the number average may be considered to be more significant. Preferably, the number average will be less than 1,000 nanometers.(less than 1 micron) and, more preferably, less than 500 nanometers (less than 0.5 micron).

Level of Graft and Entrapped Polyamide

Determined by soaking a film of the product approximately 2 mils thick in 90% formic acid/10% water once for 90 minutes and two times for 10 minutes each, then rinsing twice with distilled water and drying. Residual (grafted) nylon is determined by measuring nitrogen by the Kjehldahl method.

The method for graft level is difficult an gives approximate values. For example, mechanically I0 trapped nylon is analyzed as grafted.

Inherent Viscosity: Measured as 0.5 gms/100 ml in 90% formic acid in water at 30° C.

Number Average Molecular Weight: Molecular weight of the polyamide raw materials is determined by end group anaylsis. Molecular weight of the matrix is calculated from molecular weight of the polyamide ingredients.

Determination of Acetamide Capped End Groups

The procedure for determining acetamide end groups in low molecular weight polyamides utilizes reaction with p-toluenesulfonic acid monohydrate in ethanol at 150° C. in a sealed tube for 16 hours. In this reaction, the acetamide group is hydrolyzed to acetic acid and simultaneously esterified to produce ethyl acetate. The amount of ethyl acetate produced is then measured via capillary gas chromatography.

Determination of Carboxyl and Amine Ends

Carboxyl ends are determined by dissolving polyamide in benzyl alcohol at 170±5° C. and titrating with dilute NaOH to a phenolphthalein end point. Amine ends are determined by dissolving polyamide in 85 phenol/15 methanol mixture and titrating with dilute perchloric acid to a potentiometric end point.

EXAMPLES

The Examples, Controls and Comparisons which follow are set forth in Table format. Percentages are by weight unless otherwise indicated.

A list and description of the high molecular weight polyamides used is set forth in Table 1.

A list and description of the low molecular weight polyamide diluents used is set forth in Table 2.

A list and description of tougheners used is set forth in Table 3.

The Examples of the invention are set forth in Table 4 in tabular format.

Control experiments carried out are set forth in Table 5.

Certain comparisons are set forth in Table 6.

Details of preparation of the Examples, Controls and Comparisons are set forth in Table 7.

An explanation of the Examples, Controls and Comparisons follows:

Example 1 illustrates use of a side feeder on the 30 mm extruder to introduce the low molecular weight polyamide. The concentrate of toughener in high molecular weight polyamide is fed to the rear of the extruder. This composition has a viscosity of approximately 300 poise at a temperature of 280° C. and a shear rate of 1,000 reciprocal seconds. Its flow rate is 56 gm/10 minutes. There is some ambiguity in concentration because of fluctuations in feed rates from two volumetric feeders used to feed the concentrate and the diluent. To some degree, this is true with other examples of side feeding. Example 2 differs from Example 1 in the toughener employed and in use of dry blending rather than side feeding to add the low molecular weight polyamide. Example 3 is a duplicate of Example 2.

In all blends made with more than 25% low molecular weight polyamide, mixing may be erratic, leading to erratic results. It is, therefore, preferred to use 25% of the low molecular weight component or less, with the component of sufficiently low molecular weight to give desired increase in flow or decrease in molecular weight of the final product. Despite this problem, a number of useful and interesting examples of this invention are made with diluent levels above 25%.

The concentrate for Example 4 is made with unextracted 6 nylon and a toughener with the concentration of graft sites selected to give sufficient grafting with the polyamide without causing excessive viscosity rise. 0.3 percent of CuI/KI/aluminum distearate in the ratios 7/1/0.5 is added as a heat stabilizer. An excellent combination of mechanical properties is obtained with moderately good flow.

The experiment is repeated as Examples 5 and 6. The variability in results appears to be due to a mixing problem on the 28 mm extruder with co-fed diluent in concentrate at a ratio of 40/60.

Examples 7 and 8 are similar to 5 and 6 in overall composition but greater toughness is obtained. Reducing molecular weight of the low molecular weight polyamide by a factor of 2 permits use of smaller amounts of low molecular weight polyamide. It is likely that the lower volume fraction required of the lower molecular weight material leads to greater reliability of mixing.

Example 9 is made using a concentrate made on the 28 mm extruder with the same composition as Example 10. Although results are similar to those obtained with Example 10 where the concentrate was prepared in a larger machine, the flex modulus is 200,000 psi compared to 140,000 for Example 10. It appears likely that in small equipment, the unextracted 6 monomer is removed more effectively than in the larger machine, thereby eliminating the plasticizing effect. Examples 10 and 11 made on the 28 mm extruder are identical in composition to Examples 7 and 8 made on the 30 mm with side feed. The extruder makes no difference in this situation where the weight fraction of low molecular weight polyamide is no more than 25%. Example 12 with a calculated number average molecular weight below 5,000 is still ductile and the flow is very high. This material molds to a glossy finish at 400 psi injection pressure. Example 13 gives a similar result with a slightly higher molecular weight low molecular weight polyamide. Example 14 is a duplicate of Example 12.

Examples 15 and 16 are identical except for the screw speed in preparation of the concentrate. The concentrate for 15 is prepared at 286 rpm. The concentrate for 16 is prepared at 240 rpm. The melt temperature of the concentrate for 15 is 353° C. measured with a thermocouple probe inserted into the melt at the die. The melt strand from the dilution step for these two samples is extremely rough indicating poor mixing. The mixing problem may arise from the comparatively high volume ratio of the low viscosity diluent and the high viscosity of the concentrate caused both by the comparatively high functionality of the toughened blend as well as the high concentration. Despite the mixing problem, toughness of these materials is very good. Example 17 represents an increase in the amount of 66 nylon in the final composition.

Examples 18 and 19 show the use of very low molecular weight low molecular weight polyamide with a large number of acetamide ends to achieve a good combination of toughness and flow. In Example 20 the matrix for the concentrate comprises 66 nylon and a 66/6 copolymer while in the next example, the matrix is comprised entirely of 66 nylon. In these two experiments, a "Kenics" static mixer is attached to the end of the extruder to aid mixing.

In Example 21 the polyamide matrix has a slightly higher molecular weight than in Example 20.

The product of Example 22, made by side feeding a low molecular weight polyamide containing acetamide ends is less tough than Example 1, but flow is better

Examples 23, 24, 25 and 26 also contain only 66 nylon in the matrix. Mechanical properties are good. Compositions with mixtures of 66 and 6 nylon or 66/6 copolymer present tend to have superior combinations of flow and toughness. Example 25B is molded with about 15 minutes hold-up time in the barrel of the molding machine, rather than the customary 5 or 6 minutes. At this hold-up time at temperatures of 280° C., agglomeration of the toughener may begin to occur, adversely affecting mechanical properties. The time for this problem to occur may vary with composition.

Example 27 demonstrates the effect of hold-up time in the molding machine for approximately 5, 10 and 15 minutes (A, B, and C, respectively) with a composition which contains a mixture of 66 and unextracted 6 nylon. Example 28A, B, C also demonstrates the effect of the same variation of hold-up time. The two sets may show the effect of varying the molecular weight and flow.

Example 29 contains a concentrate prepared with comparatively high molecular weight polyamides and is diluted with a substantial amount of low molecular weight polyamide to give a good combination of mechanical properties and flow.

Example 30 demonstrates an excellent combination of mechanical properties and flow, as well as the range of variability.

Example 31 demonstrates that polyamide containing water and a polymerization catalyst, phenylphosphinic acid, with unextracted 6 nylon in the concentrate can be used.

Examples 32 through 49 are made using unextracted 6 nylon and various combinations of tougheners to prepare the concentrates. Low molecular weight polyamides include 66 and 6 nylon. Examples 46 and 48 have high acid ends. Examples where low concentrations (about 2%) of tougheners with high functionality (close to 2 weight % anhydride) are added sometimes give erratic results. The maximum toughener particle size in several examples is several microns, approaching 5 microns. Although those skilled in the art will recognize that smaller particle size, in the micron range, is generally preferred, it does not appear to be a critical parameter with the low molecular weight matrix, as long as modulus of the toughener and graft sites are controlled. Reference to Table A shows that number average particle size is likely to be below 1,000 nanometers and preferably below 500 nanometers even when some much larger particles are present. Results are erratic with low molecular weight polyamide additive levels over 25%, at least in part because of problems in mixing above this level, but a ductile product has been made at an additive level of 28% with number average molecular weight of the matrix as low as 3,100. See Example 43. An approach not used in these experiments to reduce the mixing problem is to run staged dilutions. Note that the matrix for Example 43, Control 7, Table 6, taken through the same processing steps as the toughened material, has a notched Izod of 0.25 ft lbs/inch, a tensile strength of 4.9 Kpsi and an elongation of 1.3%.

Examples 49 through 53 demonstrate that excellent combinations of mechanical properties and flow can be obtained using concentrates which contain only polyamide copolymers as the matrix.

Example 54 shows the effect of adding amorphous polyamide where amorphous polyamide content is about 20% of the total nylon present. Higher levels of amorphous content affect toughness adversely.

Example 55 demonstrates that an acrylic toughener may be employed to produce a product of this invention, though in a companion experiment with rubber content at 28%, flow is only 1/3 as great.

Example 56 demonstrates that satisfactory product can be obtained in a single extrusion process where concentrate is prepared in the back end of an extruder and diluent is added as a side stream. A static mixer is employed in this experiment to provide more mixing. It is expected that appropriate extruder screw design would be sufficient to achieve good product without use of a static mixer.

Examples 57 and 58 show that a single screw extruder run at two different screw speeds can be used to dilute a toughened concentrate to good product.

Example 59 shows that use of a single screw extruder can be extended to use a screw injection molding machine to dilute the concentrate and mold the product, but variability of the product with limited mixing may be a problem, as suggested by two flow values of 1070 and 209 grams/10 minutes.

The compositions of this invention are particularly suitable for reinforcement. Glass reinforcement is illustrated by a composition which contained 40% of the product of Example 45 and 60% OCF P553B glass. The composition could be molded into 1/8 inch test bars at 5,800 psi injection pressure. The bars had a notched Izod at the gate end of 6.8 ft. lbs/inch and 8.1 ft. lbs/inch at the far end. The modulus was 1,840,000 psi.

The compositions of this invention can be blended with commercial compositions to get improved combinations of mechanical properties and flow. A commercial polyamide/glass reinforced composition, "Zytel" 80G43L, was diluted from 43 to 33% glass by adding product of Example 45. Izod toughness was the same as that of the commercial polyamide product, "Zytel" 80G33L, and melt flow was 5.6 grams/10 minutes versus no flow for "Zytel" 80G33L in this test. Similar advantages could be expected in mineral filled and unreinforced compositions.

Controls

Controls 1 and 2 are to be compared with Example 4 in Table 4 to examine the effect of molecular weight at constant toughener concentration. Although mixing of high molecular weight diluent into concentrate in these cases would be expected to be comparatively easy, no benefit is seen in particle size or notched Izod. In this series of experiments, it appears that over more than a 3-fold range of polyamide matrix molecular weight, toughness is substantially unaffected--a remarkable conclusion.

Control 3 is another example of prior art technology with the typical flow, about two orders of magnitude less than the typical values of this invention. Control 4 is the 66 nylon matrix for Control 3.

Control 5 is untoughened polyamide matrix compared with toughened material in Table 6.

ST811HS is an example of the prior art with a matrix of unextracted 6 nylon. Again, flow is very low.

Comparison of Toughened and Untoughened Materials

Particularly dramatic examples of the advantages of this invention are presented in Table 6. The two untoughened materials, Controls 7 and 8 are processed in the same way as the toughened samples Examples 43 and 45. The untoughened materials have such low elongation and notched Izod toughness that they would have no commercial value as mechanical parts. Toughened by the techniques of the invention, however, toughness is dramatically improved and the melt flow is very high.

                  TABLE 1                                                          ______________________________________                                         HIGH MOLECULAR WEIGHT POLYAMIDES                                                                     COOH    NH2                                                                    END     END   IV   CALC                                  NUMBER  COMPOSITION   GRPS    GRPS  (2)  Mn                                    ______________________________________                                         H1      66 nylon      75      46    1.01 16,500                                H2      66 nylon      98      75    0.77 11,500                                                                    0.76                                       H3      77.5/22.5 66/6 nylon                                                                         33      33    1.56 30,000                                        copolymer                                                              H4      66 nylon      41      24    1.65 31,000                                                                    1.55                                       H5      6 nylon       35      41    1.24 26,300                                        (unextracted)                                                          H6      73/27 66/6 nylon                                                                             58      51    1.05 17,900                                        copolymer (1)                                                          H7      73/27 66/6 nylon                                                                             58      51    1.06 17,900                                        copolymer                                                              H8      6 nylon       43      54    1.19 20,600                                        (extracted)                                                            H9      amorphous     123     41    0.32 12,200                                ______________________________________                                          end group units = eq/1,000,000 gas                                             (1) 0.025% copper stearate                                                     (2) inherent viscosity                                                   

                                      TABLE 2                                      __________________________________________________________________________     LOW MOLECULAR WEIGHT POLYAMIDES MADE BY                                        AUTOCLAVE POLYMERIZATION                                                             66 NYLON  ACETIC                                                               SALT  HMD ACID COOH   NH2    ACETAMIDE                                                                              CALC                                NUMBER                                                                               LBS   (3) LBS  END GRPS                                                                              END GRPS                                                                              END GRPS                                                                               Mn                                  __________________________________________________________________________     L1    37.8  1.04                                                                               0.65 30     189    310     3780                                                                   (calc)                                      L2    37.8  1.04                                                                               0.65 22     201    310     3750                                                                   (calc)                                      L3    37.8  1.04                                                                               0.65 28     189    276     4060                                L4    37.8  2.08                                                                               1.3  40     354    620     1950                                                                   (calc)                                      L5    100   11.9                                                                               7.4  11     420    864     1540                                L6    100   3.57                                                                               2.2  25     214    338     3470                                L7    100   5.94                                                                               3.7  10     520    526     1890                                L8    100   11.9                                                                               7.4   6     504    874     1440                                L9    100   11.9                                                                               7.4   9     546    947     1330                                L10   100   11.9                                                                               7.4  10     522    949     1350                                      (1)                                                                      L11   100   11.9                                                                               7.4  12     606    951     1275                                L12   100   5.9 10.5 316     12    1219    1290                                L13   100       9    788     13            2500                                                (2)                                                            L14   100   11.9                                                                               7.4  15     375    999     1440                                L15   100   11.9                                                                               7.4  20     431    999     1380                                L16   37.8  1.38                                                                               0.87 50     254    368     2980                                __________________________________________________________________________      matrices L1 thru L10, L16 contain 0.008% antifoam "Dow Corning                 matrices L5 thru L15 contain 0.004% antifoam "Carbowax                         (1)caprolactan in lieu of 66 nylon salt                                        (2)lipic acid in lieu of acetic acid                                           (3)hexamethylenediamine                                                  

                                      TABLE 3                                      __________________________________________________________________________     TOUGHENERS                                                                                          MELT FLOW(2)                                                                            TENSILE MODULUS                                  NUMBER                                                                               COMPOSITION    gm/10 min                                                                               ASTM D882 Kpsi                                   __________________________________________________________________________     T1    E/P/Hexadiene  1        1.146                                                  Norbornadiene-g-MAnh                                                           ca68(ca27/4.1/0.4-                                                       T2    E/nBa/MAA      9        3.837                                                  70.7/21/8.3                                                                    (54-55% Zinc                                                                   neutralization)                                                          T3    E/P/Hexadiene/ 2.4      1.659                                                  Norbornadiene-g-MAnh                                                           ca68/ca27/4.1/0.4-                                                             0.34/26/ca6.3/0.15                                                       T4    E/P/Hexadiene/ 0.3      1.027                                                  Norbornadiene                                                                  ca68/26/ca6.3/0.15                                                       T5    Cyanacryl C(1) 0.6      0.07                                                   (AMERICAN CYANAMID)                                                      T6    T8, 50%/T9, 50%                                                                               1.5      1.152                                            T7    T1, 50%/T9, 50%                                                                               0.6      0.784                                            T8    E/P/Hexadiene/ 5        1.587                                                  Norbornadiene-g-MAnh                                                           ca68/ca27/4.1/0.4-                                                             2.45 (acid & anhydride)                                                  T9    E/P/Hexadiene  2.9      0.13                                                   53/ca42/ca4.7                                                            __________________________________________________________________________      (1)used 2% (by weight) 5MA3000(ARCO)styrene/maleic anhydride copolymer         (25% Ma)                                                                       (2)ASTM D 1238 Condition G                                                     Cyanacryl Cpolyacrylic rubber                                                  E--ethylene                                                                    P--propylene                                                                   nBa--normal butyl acrylate                                                     MAA--methyacrylic acid                                                   

                                      TABLE 4                                      __________________________________________________________________________     EXAMPLES                                                                       __________________________________________________________________________                                           MATRIX   END  GRAFT SAXS                 NUM- TOUGHENER                                                                              MATRIX      %      MATRIX                                                                               IMBALANCE +                                                                             GROUP                                                                               LEVELS                                                                               nano                 BER  NUMBER(S)                                                                              NUMBER(S)   LMWN(1)                                                                               Mn    CAPPED ENDS                                                                             RATIO                                                                               %     meters               __________________________________________________________________________      1   T6, 20% H3, 30%     50     5600  294      4.2  5.71  241                               L1, 50%                                                            2   T2, 20% H3, 30%     50     5600  294      4.2  5.18  306                               L1, 50%                                                            3   T2, 20% H3, 30%     50     5600  294      4.2  3.01  382                               L1, 50%                                                            4   T3, 16.8%                                                                              H5, 43.2%   40     6800  238      4.1  1.58  403                               L2, 40.0%                                                          5   T3, 16.8%                                                                              H5, 43.2%   40     7200  213      3.5  7.01  335                               L3, 40.0                                                           6   T3, 16.8%                                                                              H5, 43.2%   40     7200  213      3.5  5.5   349                               L3, 40.0%                                                          7   T3, 21% H5, 54%     25     5300  299      3.8  3.42  282                               L4, 25%                                                            8   T3, 22% H5, 58%     20     6300  244      3.3  5.86  284                               L4, 20%                                                            9   T3, 21.0%                                                                              H5, 54.0%   25     5300  300      3.8  4.82  262                               L4, 25.0%                                                         10   T3, 21.0%                                                                              H5, 54.0%   25     5300  300      3.8  2.75  333                               L4, 25.0%                                                         11   T3, 22.4%                                                                              H5, 57.4%   20     6200  246      3.4  3.11  329                               L4, 20.0%                                                         12   T3, 19.6%                                                                              H5, 50.4%   30     4600  352      4.3  2.40  349                               L4, 30.0%                              2.33                       13   T3, 18.2%                                                                              H5, 46.8%   35     6000  249      3.2  3.71  347                               L16, 35.0%                             5.76                       14   T3, 19.6%                                                                              H5, 50.4%   30     4600  352      4.3  1.78  341                               L4, 30%                                                           15   T7, 26% H3, 39.0%   35     6000  271      3.3  5.56  865/258                           L16, 35%                                     (2)                  16   T7, 26% H3, 39.0%   35     6000  271      3.3  3.02  930/252                           L16, 35.0%                                   (2)                  17   T3, 22.0%                                                                              H3, 24.0%/H1, 12.0%                                                                        30     4500  353      3.6  3.71  282                               H4, 12.0%/L4, 30.0%                                               18   T3, 23.8%                                                                              H5, 61.2%   15     6300  259      3.8  4.24  326                               L5, 18.0%                                                         19   T3, 23.0%                                                                              H5, 59.0%   18     5500  303      4.4  2.8   329                               L5, 18.0%                                                         20   T3, 26.0%                                                                              H6, 31.0%/H1, 31.0%                                                                        12     6500  191      1.9  4.02  509                               L5, 12.0%                                                         21   T3, 26.0%                                                                              H4, 31.0%/H1, 31.0%                                                                        12     7100  139      1.9  5.82  359                               L5, 12.0%                                                         22   T3, 18% H5, 47%     35     6900  228      3.7  3.76  367                               L6, 35%                                                           23   T3, 26.0%                                                                              H1, 31%/H4, 31%                                                                            12     7100  139      1.9  5.22  336                               L5, 12%                                                           24   T3, 25.0%                                                                              H4, 29.0%/H1, 29.0%                                                                        18     5300  284      2.7  6.12  402                               L5, 18.0%                                                         25A  T3, 26.0%                                                                              H4, 31.0%/H1, 31.0%                                                                        12     7100  187      1.9  9.57  349                               L5, 12.0%                                                         25B  T3, 26.0%                                                                              H4, 31.0%/H1, 31.0%                                                                        12     7100  187      1.9  4.41  382                               L5, 12.0%                                                         26   T3, 25.5%                                                                              H1, 59.5%   15     5600  233      2    3.74  471                               L5, 15.0%                                                         27A  T3, 24.6%                                                                              H5, 63.4%   12     7400  207      3.2  5.09  309                               L5, 12.0%                                                         27B  T3, 24.6%                                                                              H5, 63.4%   12     7400  207      3.2  3.73  310                               L5, 12.0%                                                         27C  T3, 24.6%                                                                              H5, 63.4%   12     7400  207      3.2  8.3   315                               L5, 12.0%                                                         28A  T4, 19.0%                                                                              H8, 55.3%   21     4100  415      5.6  2.64  339                       T1, 4.7%                                                                               L9, 21.0%                              2.64                       28B  T4, 19,0%                                                                              H8, 55.3%   21     4100  415      5.6  2.32  371                       T1, 4.7%                                                                               L9, 21.0%                              2.44                       28C  T4, 19,0%                                                                              H8, 55.3%   21     4100  415      5.6  2.78  419                       T1, 4.7%                                                                               L9, 21.0%                              2.85                       29   T3, 22.5%                                                                              H4, 26.3%/H3, 26.3%                                                                        25     5200  328      6.6  3.73  732/226                           L7, 25.0%                                    (2)                  30   T3, 22.5%                                                                              H5, 52.5%   25     5100  339      7.2  2.47  268                               L7, 25.0%                                                         31   T3, 25.5%                                                                              H3, 29.8%/H1, 29.8%                                                                        15     5700  265      3    3.6   313                               L8, 15.0%                                                         32   T3, 22.5%                                                                              H8, 52.5%   25     4900  339      6.3  3.7   238                               L7, 25.0%                                                         33   T4, 20.4%                                                                              H8, 59.5%   15     5300  307      4.2  3.37  374                       T1, 5.1%                                                                               L9, 15.0%                                                         34   T4, 19.0%                                                                              H8, 55.3%   21     4100  415      5.6  3.64  359                       T1, 4.7%                                                                               L9, 21%                                                           35   T4, 23.8%                                                                              H8, 59.5%   15     5300  307      4.2  1.74  >1000                     T1, 1.7%                                                                               L9, 15.0%                                                         36   T3, 25.5%                                                                              H8, 59.5%   15     5300  307      4.1  3.44  257                               L10, 15.0%                                                        37   T4, 23.0%                                                                              H8, 59.5%   15     5300  307      4.1  2.53  539                       T1, 2.6%                                                                               L10, 15.0%                             2.12                       38   T4, 23.8%                                                                              H8, 59.5%   15     5300  307      4.1  1.77  >1000                     T1, 1.7%                                                                               L10, 15.0%                                                        39   T4, 20.4%                                                                              H8, 59.5%   15     5300  307      4.1  3.81  348                       T1, 5.1%                                                                               L10, 15.0%                             3.81                       40   T7, 18.2%                                                                              H8, 53.2%   24     3800  469      6.4  4.07  346                               L9, 24.0%                              3.23                       41   T4, 17.5%                                                                              H8, 51.1%   27     3400  521      7.2  4.07  348                       T1, 4.4%                                                                               L9, 27.0%                                                         42   T4, 13.0%/T3,                                                                          H8, 46.8%   28     3100  585      8.3  4.04  311                       10.1%                                                                          T1, 2.2%                                                                               L11, 28%                                                          43   T4, 13.0%/T3,                                                                          H8, 46.8%   28     3100  553      8.3  3.14  304                       10.1%                                                                          T1, 2.2%                                                                               L11, 28.0%                                                        44   T4, 13.7%/T3,                                                                          H8, 49.4%   24     3500  491      3.3  2.26  299                       10.6%                                                                          T1, 2.2%                                                                               L12, 24.0%                                                        45   T4, 13.7%/T3,                                                                          H8, 49.4%   24     3500  512      7.1  4     318                       10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        46   T4, 14.2%/T3,                                                                          H8, 51.4%   21     6800  216      6.2  2.12  367                       11.1%                                                                          T1, 2.4%                                                                               L13, 21.0%                             2.19                       47   T4, 13.7%/T3,                                                                          H8, 49.4%   24     3500  512      7.1  3.89  309                       10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        48   T4, 14.2%/T3,                                                                          H8, 51.4%   21     6800  216      6.2  3.4   367                       11.1%                                                                          T1, 2.4%                                                                               L13, 21.0%                                                        49   T4, 13.7%/T3,                                                                          H7, 33.1%/H3, 16.3%                                                                        24     3700  474      5.5  3.24  507                       10.6%                                                                          T1, 2.2%                                                                               L10, 24.0%                                                        50   T3, 26.6%                                                                              H7, 33.1%/H3, 16.3%                                                                        24     3500  502      6.1  3.96  575                               L11, 24.0%                                                        51   T4, 13.7%/T3,                                                                          H7, 37.0%/H3, 12.4%                                                                        24     3500  501      5.6  3.05  634                       10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        52   T4, 13.7%/T3,                                                                          H7, 39.5%/H3, 9.9%                                                                         24     3500  501      5.8  2.88  633                       10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        53   T4, 13.7%/T3,                                                                          H7, 33.1%/H3, 16.3%                                                                        24     3500  502      6.1  2.94  619                       10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        54   T4, 13.7%/T3,                                                                          H3, 34.2%/H9, 15.2%                                                                        24     3900  427      3.2  33.6  >1000                     10.6%                                                                          T1, 2.3%                                                                               L11, 24.0%                                                        55   T7, 25.4%                                                                              H1, 29.65%/H3, 29.65%                                                                      15.3   5200  324      3.2  3.16  419                               L12, 15.3%                                   (3)                  56   T3, 25% H1, 30%/H3, 30%                                                                            15     5600  271      2.5  2.74  653                               L15, 15%                               2.93                       57   T3, 23.5%                                                                              H5, 60.5%   16     5500  299      3.8  2.78  377                               L15, 16.0%                                                        58   T3, 23.5%                                                                              H5, 60.5%   16     5500  299      3.8  3.36  311                               L15, 16.0%                                                        59   T3, 23.8%                                                                              H5, 61.2%   15     6000  275      4.5  5.74  352                               L8, 15.0%                                                         __________________________________________________________________________          MAXIMUM TEN     %    GATE FAR  TENSILE                                                                               ELONGA-                                                                              FLEXURAL                      NUM- PARTICILE SIZE                                                                           FLOW  water                                                                               IZOD IZOD STRENGTH                                                                              TION  MODULUS                                                                               PRODUCT                BER  nanometers                                                                               gm/10 min                                                                            (4)  ft lbs/in                                                                           ft lbs/in                                                                           Kpsi   %     Kpsi   (5)                    __________________________________________________________________________      1    700       56   0.024                                                                               14.8 14.6 6.5    57    257     5400                   2   3600      606   0.017                                                                               3.2  3.4  7.4    24    270    15700                   3   1700      460   0.005                                                                               3.2  3.3  7.4    25    260    10900                   4    600      480   0.018                                                                               14.6 14.9 6.8    80    274    47300                   5   1400      610   0.02 8.2  7.2  7.6    51    180    38000                   6   1000      600   0.04 4.9  6.6  6.7    51    204    19600                   7   1300      400   0.002                                                                               12.1 12.2 5.4    76    132    26400                   8    800      190   0.007                                                                               13.5 14.2 5.3    120   124    13800                   9    800      470   0.004                                                                               13.4 13.2 6.1    49    204    38000                  10   1700      630   0.017                                                                               11.8 12.5 5.4    102   141    40100                  11   1100      270   0.008                                                                               13.1 13.8 5.2    123   132    18500                  12   1500      580   0.021                                                                               10.8 11   5.6    99    146    35200                  13   1200      510   0.013                                                                               9.7  10.1 6      100   162    29900                  14   1300      590   0.012                                                                               8.9  8.7  6.1    72    181    32000                  15   2000      180   0.025                                                                               16.2 16.1 5.4    62    200    15400                  16   1500      140   0.016                                                                               16.2 16.3 5.4    71    193    12300                  17   1500      550   0.015                                                                               10.7 10.4 6.7    22    247    39600                  18   1500      220   0.019                                                                               11   11.6 5.4    85    169    12900                  19   1300      350   0.028                                                                               10.3 10.3 5.5    89    182    20000                  20   1300      170   0.032                                                                               12   11.9 5.6    37    214    11700                  21   2400      110   0.014                                                                               12.2 12.6 6      38    242     8100                  22    600      250   0.008                                                                               9.7  9.6  6.7    60    160    15900                  23   2400       83   0.02 14   14   6.4    37    244     7400                  24   1400      320   0.018                                                                               8    10.3 6.4    20    261    16200                  25A  2500       89   0.012                                                                               14   14.2 6.3    31    252     7800                  25B  1300      140   0.002                                                                               10.3 10.4 5.8    24    230     8600                  26   3600      290   0.017                                                                               9.7  9.89 6.2    12.6  248    17400                  27A  1700      110   0.003                                                                               12.1 12.9 5.6    131   121     7300                  27B  1400      130   0.003                                                                               11.1 11.8 5.4    115   118     7700                  27C  1400      210   0.014                                                                               10.1 10.2 5.5    99    121    11600                  28A   800      320   0.004                                                                               17.8 18   5.6    46    200    32100                  28B  1200      330   0.001                                                                               15.4 15.3 4.9    36    183    24500                  28C  1900      310   0.001                                                                               3.5  3.8  4.8    27    180     5200                  29   1800      320   0.009                                                                               11.1 11.3 6.4    26    247    22400                  30   1000      390   0.01 12.3 12.2 5.5    78    193    26200                  31   2500      130   0.029                                                                               11.4 11.4 5.5    21    207     8300                  32    900      500   0.016                                                                               12.1 12   6.5    36    239    39600                  33   1000      230   0.018                                                                               19.2 19.4 5.9    47    221    26400                  34    900      520   0.019                                                                               17.8 18.3 5.9    50    222    54600                  35   4700      260   0.013                                                                               11.4 11.8 5.2    58    203    15500                  36   1400      370   0.016                                                                               10.2 10.2 5.9    29    201    22000                  37   3200      480   0.01 14.9 15   5.3    63    196    37500                  38   3900      420   0.019                                                                               4    11   5      49    205     8400                  39   1000      280   0.022                                                                               18.1 18.8 5.8    39    206    29200                  40   1200      770   0.008                                                                               16.3 15.8 5.6    46    205    70300                  41   1000      1050  0.021                                                                               16.2 15.6 5.7    38    211    96500                  42   1400      830   0.001                                                                               11.9 11.6 5.3    28    192    52300                  43   1200      820   0.025                                                                               13.3 12.4 5.4    30    190    58900                  44   1300      1410  0.027                                                                               3.4  3.3  5.3    25    183    25500                  45   1000      800   0.009                                                                               13.2 13.4 5.3    37    196    55900                  46   2300      1080  0.01 4.4  7.2  4.9    26    185    23300                  47   1400      830   0.006                                                                               12.9 12.4 5.3    29    197    56600                  48   3300      1060  0.016                                                                               2.1  5.1  4.8    27    174    10700                  49   2200      430   0.012                                                                               4.5  4.4  4      44    118     7700                  50   2400      480   0.014                                                                               11   11   4.9    25    180    26000                  51   1900      520   0.014                                                                               10.2 11.3 4.8    26    190    25300                  52   2400      480   0.009                                                                               2.6  4.6  4.8    20    187     6000                  53   2300      830   0.005                                                                               11.2 11.6 4.8    25    187    44700                  54   2500      310   0.006                                                                               10.8 11.1 5.6    41    204    18600                  55    930      550   0.003                                                                               3.5  3.6  6.3    45            1200                  56   4200      310   0.008                                                                               9.2  9.5  6.4    31    223    18000                  57   1400      430   0.015                                                                               11.4 11.7 5.2    66    130    25300                  58   2200      200   0.009                                                                               11.7 13.2 4.4    93    90     10000                  59   2400      210   0.004                                                                               14   14.6 4.6    120          13500                  __________________________________________________________________________      (1)LMWN--low molecular weight nylon                                            (2)bimodal distribution                                                        (3) signifigant number of particles >1000 nm                                   (4)% moisture for flow measurement                                             (5)PRODUCT(GATE IZOD)(TENSILE STRENGTH)(FLOW)                            

                                      TABLE 5                                      __________________________________________________________________________     CONTROLS                                                                       __________________________________________________________________________                                    MATRIX                                                                         IMBAL-                                                                         ANCE +                                                                               END  GRAFT SAXS MAXIMUM TEN               NUM-                                                                               TOUGHENER                                                                              MATRIX %     MATRIX                                                                               CAPPED                                                                               GROUP                                                                               LEVELS                                                                               nano PARTICILE SIZE            BER NUMBER(S)                                                                              NUMBER(S)                                                                             LMWN(1)                                                                              Mn    ENDS  RATIO                                                                               %     meters                                                                              nanometers                __________________________________________________________________________     C1  T3, 16.8%                                                                              H5, 43.2%                                                                             40    20500 11    1.2  12.36 247  2400                                  H1, 40.0%                                                          C2  T3, 16.8%                                                                              H5, 43.2%                                                                             40    16200  8    1.1  4.96  294  1400                                  H2, 40.0%                                                          C3  T4, 10.0%                                                                              H1, 81.0%                                                                              0    16500 29    1.6  5.61  385  1500                          T1, 9.0%                                                                   C4  (1)     H1, 100.0%                                                                             0    16500 29    1.6  (1)   (1)  (1)                       C5  (1)     H8, 71%                                                                               29     3800 456   6.3  (1)   (1)  (1)                                   L11, 29%                                                           C6  T3, 28% H5, 72%      26300  5    1.2  11.74      1400                      __________________________________________________________________________                        %   GATE FAR  TENSILE         FLEXURAL                               NUM-                                                                               FLOW  water                                                                              IZOD IZOD STRENGTH                                                                              ELONGATION                                                                              MODULUS                                                                               PRODUCT                         BER gm/10 min                                                                            (4) ft lbs/in                                                                           ft lbs/in                                                                           Kpsi   %        Kpsi   (5)                    __________________________________________________________________________              C1  27    0.006                                                                              13.8 15.4 7.6    95       237    2830                            C2  49    0.03                                                                               13.1 14.7 7.4    80       236    4750                            C3   8    0.022                                                                              18.3 20.7 7.3    50       231    1070                            C4  94    0.024                                                                               1.2 0.7  12.4   38       405     920                                55    0.015                                                                              (5)                                                              C5  2330  0.026                                                                               0.25                                                                               0.25 8.5    2.82     360    4950                            C6   6    0.013                                                                              19.7 20.2 7.1    266      91     940                    __________________________________________________________________________      (1)control, no toughener                                                       (2)LMWN--low molecular weight nylon                                            (3)% % moisture for flow measurement                                           (4)PRODUCT(GATE IZOD)(TENSILE STRENGTH)(FLOW)                                  (5)normal value 1.0                                                      

                                      TABLE 6                                      __________________________________________________________________________     COMPARISON OF TOUGHENED AND UNTOUGHENED EXAMPLES                               __________________________________________________________________________                                     MATRIX                                                                         IMBAL-                                                                     MA- ANCE +                                                                               END  GRAFT SAXS                                                                               MAXIMUM TEN               NUM-                                                                               TOUGHENER  MATRIX %     TRIX                                                                               CAPPED                                                                               GROUP                                                                               LEVELS                                                                               nano                                                                               PARTICILE SIZE            BER NUMBER(S)  NUMBER(S)                                                                             LMWN(5)                                                                              Mn  ENDS  RATIO                                                                               %     meters                                                                             nanometers                __________________________________________________________________________     43  T4, 13.0%/T3, 10.1%                                                                       H8, 46.8%                                                                             28    3100                                                                               553   8.3  3.14  304 1200                          T1, 2.2%   L11, 28.0%                                                      C7  (1)        H8, 62.6%                                                                             37.4  3100                                                                               553   8.3  (1)   (1) (1)                                      L11, 37.4%                                                      45  T4, 13.7%/T3, 10.6%                                                                       H8, 49.4%                                                                             24    3500                                                                               512   7.1  4     318 1000                          T1, 2.3%   L11, 24.0%                                                      C8  (1)        H8, 67.3                                                                              32.7  3500                                                                               512   7.1  (1)   (1) (1)                                      L11, 32.7%                                                      __________________________________________________________________________                        %   GATE FAR  TENSILE         FLEXURAL                               NUM-                                                                               FLOW  water                                                                              IZOD IZOD STRENGTH                                                                              ELONGATION                                                                              MODULUS                                                                               PRODUCT                         BER gm/10 min                                                                            (4) ft lbs/in                                                                           ft lbs/in                                                                           Kpsi   %        Kpsi   (5)                    __________________________________________________________________________              43    820 0.025                                                                              13.3 12.4 5.4    30       190    58900                           C7  >4000     0.25 0.25 4.9    1.3      365                                    45    800 0.009                                                                              13.2 13.4 5.3    37       196    55900                           C8  >4000     0.44 0.31 7.4    2.6      372                           __________________________________________________________________________      (1)comparison, no toughener                                                    (2)LMWN--low molecular weight nylon                                            (3)% % moisture for flow measurement                                           (4)PRODUCT(GATE IZOD)(TENSILE STRENGTH)(FLOW)                            

                                      TABLE 7                                      __________________________________________________________________________                                          CONCEN-                                                                              CONCEN-                                                                  TRATE TRATE LMWN(5)                                                                               LMWN(5)                NUM- TOUGHENER  MATRIX      %        EXT.  EXT.  ADDITION                                                                              ADDITION               BER  NUMBER(S)  NUMBER(S)   STABILIZER(4)                                                                           TYPE  RPM   EXT. TYPE                                                                             EXT.                   __________________________________________________________________________                                                             RPM                    1    T6, 20%    H3, 30%     0        28 mm 300   30 mm  377                                    L1, 50%                                                         2   T2, 20%    H3, 30%     0        28 mm 300   28 mm  286                                    L1, 50%                                                         3   T2, 20%    H3, 30%     0        28 mm 300   28 mm  284                                    L1, 50%                                                         4   T3, 16.8%  H5, 43.2%   0.216    83 mm 290   28 mm  284                                    L2, 40.0%                                                       5   T3, 16.8%  H5, 43.2%   0.216    83 mm 290   28 mm  284                                    L3, 40.0                                                        6   T3, 16.8%  H5, 43.2%   0.5      83 mm 290   28 mm  286                                    L3, 40.0%                                                       7   T3, 21%    H5, 54%     0.5      83 mm 290   30 mm  377                                    L4, 25%                                                         8   T3, 22%    H5, 58%     0.5      83 mm 290   30 mm  377                                    L4, 20%                                                         9   T3, 21.0%  H5, 54.0%   0.5      28 mm 286   28 mm  286                                    L4, 25.0%                                                      10   T3, 21.0%  H5, 54.0%   0.5      83 mm 290   28 mm  286                                    L4, 25.0%                                                      11   T3, 22.4%  H5, 57.4%   0.5      83 mm 290   28 mm  286                                    L4, 20.0%                                                      12   T3, 19.6%  H5, 50.4%   0.5      83 mm 290   28 mm  286                                    L4, 30.0%                                                      13   T3, 18.2%  H5, 46.8%   0.5      83 mm 290   28 mm  286                                    L16, 35.0%                                                     14   T3, 19.6%  H5, 50.4%   0.5      83 mm 290   28 mm  285                                    L4, 30%                                                        15   T7, 26%    H3, 39.0%   0.5      28 mm 286   28 mm  285                                    L16, 35%                                                       16   T7, 26%    H3, 39.0%   0.5      28 mm 240   28 mm  285                                    L16, 35.0%                                                     17   T3, 22.0%  H3, 24.0%/H1, 12.0%                                                                        0.5      28 mm 286   28 mm  285                                    L4, 12.0%/L4, 30.0%                                            18   T3, 23.8%  H5, 61.2%   0.5      83 mm 290   28 mm  280                                    L5, 15.0%                                                      19   T3, 23.0%  H5, 59.0%   0.5      83 mm 290   28 mm  280                                    L5, 18.0%                                                      20   T3, 26.0%  H6, 31.0%/H1, 31.0%                                                                        0.31     28 mm 280   28 mm  280                                    L5, 12.0%                                                      21   T3, 26.0%  H4, 31.0%/H1, 31.0%                                                                        0.31     28 mm 284   28 mm  280                                    L5, 12.0%                                                      22   T3, 18%    H5, 47%     0.5      83 mm 290   30 mm  400                                    L6, 35%                                                        23   T3, 26.0%  H1, 31%/H4, 31%                                                                            0.5      28 mm 284   28 mm  280                                    L5, 12%                                                        24   T3, 25.0%  H4, 29.0%/H1, 29.0%                                                                        0.5      28 mm 280   28 mm  284                                    L5, 18.0%                                                      25A  T3, 26.0%  H4, 31.0%/H1, 31.0%                                                                        0.5      28 mm 284   28 mm  284                                    L5, 12.0%                                                      25B  T3, 26.0%  H4, 31.0%/H1, 31.0%                                                                        0.5      28 mm 284   28 mm  284                                    L5, 12.0%                                                      26   T3, 25.5%  H1, 59.5%   0.5      28 mm 284   28 mm  284                                    L5, 15.0%                                                      27A  T3, 24.6%  H5, 63.4%   0.5      83 mm 290   28 mm  280                                    L5, 12.0%                                                      27B  T3, 24.6%  H5, 63.4%   0.5      83 mm 290   28 mm  280                                    L5, 12.0%                                                      27C  T3, 24.6%  H5, 63.4%   0.5      83 mm 290   28 mm  280                                    L5, 12.0%                                                      28A  T4, 19.0%  H8, 55.3%   0        28 mm 284   28 mm  284                         T1, 4.7%   L9, 21.0%                                                      28B  T4, 19,0%  H8, 55.3%   0        28 mm 284   28 mm  284                         T1, 4.7%   L9, 21.0%                                                      28C  T4, 19,0%  H8, 55.3%   0        28 mm 284   28 mm  284                         T1, 4.7%   L9, 21.0%                                                      29   T3, 22.5%  H4, 26.3%/H3, 26.3%                                                                        0.5      28 mm 284   28 mm  284                                    L7, 25.0%                                                      30   T3, 22.5%  H5, 52.5%   0        28 mm 284   28 mm  284                                    L7, 25.0%                                                      31   T3, 25.5%  H3, 29.8%/H1, 29.8%                                                                        0        28 mm 284   28 mm  284                                    L8, 15.0%                                                      32   T3, 22.5%  H8, 52.5%   0.5      28 mm 284   28 mm  284                                    L7, 25.0%                                                      33   T4, 20.4%  H8, 59.5%   0        28 mm 284   28 mm  284                         T1, 5.1%   L9, 15.0%                                                      34   T4, 19.0%  H8, 55.3%   0        28 mm 284   28 mm  284                         T1, 4.7%   L9, 21%                                                        35   T4, 23.8%  H8, 59.5%   0        28 mm 284   28 mm  284                         T1, 1.7%   L9, 15.0%                                                      36   T3, 25.5%  H8, 59.5%   0        28 mm 284   28 mm  284                                    L10, 15.0%                                                     37   T4, 23.0%  H8, 59.5%   0        28 mm 284   28 mm  284                         T1, 2.6%   L10, 15.0%                                                     38   T4, 23.8%  H8, 59.5%   0        28 mm 284   28 mm  284                         T1, 1.7%   L10, 15.0%                                                     39   T4, 20.4%  H8, 59.5%   0        28 mm 284   28 mm  284                         T1, 5.1%   L10, 15.0%                                                     40   T7, 18.2%  H8, 53.2%   0        28 mm 284   28 mm  284                                    L9, 24.0%                                                      41   T4, 17.5%  H8, 51.1%   0        28 mm 284   28 mm  284                         T1, 4.4%   L9, 27.0%                                                      42   T4, 13.0%/T3,                                                                             H8, 46.8%   0        28 mm 284   28 mm  284                         10.1%                                                                          T1, 2.2%   L11, 28%                                                       43   T4, 13.0%/T3,                                                                             H8, 46.8%   0        28 mm 200   28 mm  280                         10.1%                                                                          T1, 2.2%   L11, 28.0%                                                     44   T4, 13.7%/T3,                                                                             H8, 49.4%   0        28 mm 200   28 mm  280                         10.6%                                                                          T1, 2.2%   L12, 24.0%                                                     45   T4, 13.7%/T3,                                                                             H8, 49.4%   0        28 mm 200   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     46   T4, 14.2%/T3,                                                                             H8, 51.4%   0        28 mm 284   28 mm  284                         11.1%                                                                          T1, 2.4%   L13, 21.0%                                                     47   T4, 13.7%/T3,                                                                             H8, 49.4%   0        28 mm 284   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     48   T4, 14.2%/T3,                                                                             H8, 51.4%   0        28 mm 284   28 mm  284                         11.1%                                                                          T1, 2.4%   L13, 21.0%                                                     49   T4, 13.7%/T3,                                                                             H7, 33.1%/H3, 16.3%                                                                        0        28 mm 200   28 mm  280                         10.6%                                                                          T1, 2.2%   L10, 24.0%                                                     50   T3, 26.6%  H7, 33.1%/H3, 16.3%                                                                        0        28 mm 280   28 mm  284                                    L11, 24.0%                                                     51   T4, 13.7%/T3,                                                                             H7, 37.0%/H3, 12.4%                                                                        0        28 mm 280   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     52   T4, 13.7%/T3,                                                                             H7, 39.5%/H3, 9.9%                                                                         0        28 mm 280   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     53   T4, 13.7%/T3,                                                                             H7, 33.1%/H3, 16.3%                                                                        0        28 mm 280   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     54   T4, 13.7%/T3,                                                                             H3, 34.2%/H9, 15.2%                                                                        0        28 mm 280   28 mm  284                         10.6%                                                                          T1, 2.3%   L11, 24.0%                                                     55   T7, 25.4%  H1, 29.65%/H3, 29.65%                                                                      0        28 mm 280   28 mm  280                                    L12, 15.3%                                                     56   T3, 25%    H1, 30%/H3, 30%                                                                            0        30 mm 300                                                 L15, 15%             1 step                                                                               1 step                              57   T3, 23.5%  H5, 60.5%   0        83 mm 290   2" single                                                                              30                                    L15, 16.0%                       screw                         58   T3, 23.5%  H5, 60.5%   0        83 mm 290   2" single                                                                              60                                    L15, 16.0%                       screw                         59   T3, 23.8%  H5, 61.2%   0        83 mm 290   (2)                                           L8, 15.0%                                                      C1   T3, 16.8%  H5, 43.2%   0        83 mm 290   28 mm  284                                    H1, 40.0%                                                      C2   T3, 16.8%  H5, 43.2%   0        83 mm 290   28 mm  284                                    L1, 40.0%                                                      C3   T4, 10.0%  H1, 81.0%   0        28 mm 200                                      T1, 9.0%                                                                  C4   (3)        H1, 100.0%  0        28 mm 200                                 C5   (3)        H8, 71%                          28 mm  284                                    L11, 29%                                                       C6   T3, 28%    H5, 72%     0        83 mm 290                                 C7   (3)        H8, 62.6%                        28 mm  280                                    L11, 37.4%                                                     C8   (3)        H8, 67.3                         28 mm  280                                    L11, 32.7%                                                     __________________________________________________________________________      (1)extruded with 0.75% water + 0.15% phenylphosphinic acid added               (2)unextruded, dry blended and molded                                          (3)control, no toughener                                                       (4)stabilizierKl/Cul/aluminum distearate 7/1/0.5                               (5)LMWN--low molecular weight nylon                                       

I claim:
 1. A process comprising:(a) mixing a high molecular weight polyamide or mixture of polyamides, having a number average molecular weight over 10,000, and having an inherent viscosity greater than 0.7 deciliters/gm, with an organic polymeric toughener having a tensile modulus below 10,000 or a mixture of tougheners having an average tensile modulus below 10,000, and having graft sites selected from metal neutralized carboxyl, adjacent carboxyl, anhydride or epoxy groups in a melt extruder at shear forces sufficient to dispense the toughener in the polyamide such that the toughener has a number average particle size below about 1,000 nanometers measured by Transmission Electron Microscope (TEM); and (b) blending into the blend obtained in step (a), a low molecular weight polyamide which will react by transamidation having a number average molecular weight below 5,000 an having an inherent viscosity less than 0.5 said polyamide being chosen to have a sufficiently low molecular weight to result, after reaction with the polyamide in step (a), in a polyamide matrix wherein the number average molecular weight is below 8,000. 